WO2010059287A2 - Abrasion resistant composition - Google Patents
Abrasion resistant composition Download PDFInfo
- Publication number
- WO2010059287A2 WO2010059287A2 PCT/US2009/057630 US2009057630W WO2010059287A2 WO 2010059287 A2 WO2010059287 A2 WO 2010059287A2 US 2009057630 W US2009057630 W US 2009057630W WO 2010059287 A2 WO2010059287 A2 WO 2010059287A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal
- carbide particles
- surface covering
- introduction
- weight
- Prior art date
Abstract
Description
Claims