US20130122461A1 - Medical cutting tool - Google Patents
Medical cutting tool Download PDFInfo
- Publication number
- US20130122461A1 US20130122461A1 US13/813,399 US201113813399A US2013122461A1 US 20130122461 A1 US20130122461 A1 US 20130122461A1 US 201113813399 A US201113813399 A US 201113813399A US 2013122461 A1 US2013122461 A1 US 2013122461A1
- Authority
- US
- United States
- Prior art keywords
- brazing
- joint
- neck
- shank
- cutting tool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
[Problem] To provide a method for manufacturing a medical cutting tool and a medical cutting tool that will not rust and that is capable of stably demonstrating high strength.
[Solution] A working section (2) formed by a cemented carbide or ceramic is brazed to the tip of a shank part (1) formed by a round bar-shaped austenitic stainless steel, thereby constituting a cutting tool (A). The shank part (1) comprises a shank (1 a), a neck (1 b), and a joint (1 c) to which the working section (2) is brazed. At least part of the stainless steel near the joint (1 c) of the neck (11 b) and in the joint (1 c) has a fiber-like structure. The structure of the stainless steel in the joint (1 c) on the working section (2) side has a granular structure.
Description
- The present invention relates to a medical cutting tool which is used to cut a surface layer of a tooth, a bone including an alveolar bone, and the like used during dental treatment.
- In a dental treatment, a desired treatment may be performed by cutting a surface layer of a tooth. A medical cutting tool used during the treatment includes a shank portion gripped by a chuck of a handpiece, and a working portion continuously formed from the shank portion and including a cutting blade which is formed from an outer circumference to a leading end portion and is used to cut a surface layer. The medical cutting tool formed as described above is fixed to the handpiece when the shank portion is gripped by the chuck. Then, by an operation of a doctor, the rotating working portion is pressed to a portion to be treated, thereby cutting a desired portion.
- In the medical cutting tool, the working portion needs to ensure a sufficient cutting performance with respect to a hard surface layer. Thus, in general, the working portion is formed using cemented carbide represented by tungsten carbide. The shank portion needs to ensure a strength that can sufficiently resist bending and warping affected when a desired portion is cut by the working portion. When the working portion is formed using cemented carbide to improve the strength of the shank portion, it is preferable that the shank portion be formed continuously from the working portion and using cemented carbide.
- However, there occurs a problem that the time used to process the cemented carbide in a shape corresponding to the medical cutting tool takes long. Thus, the shank portion is formed using, for example, SUS 420 which is martensitic stainless steel or carbon tool steels (SK), an intermediate component used to form the working portion is formed by cemented carbide, and the intermediate component of the working portion is bonded to a leading end of the shank portion by pressure welding, so that a medical cutting tool processed in a desired shape is provided.
- As described above, when stainless steel or tool steel and cemented carbide are bonded to each other, an optimum method corresponding to a material to be bonded is selected and employed from methods such as pressure welding including friction pressure welding and heating pressure welding, resistance welding, and brazing in general.
- When stainless steel or carbon steel forming the shank portion and cemented carbide forming the working portion are bonded to each other using friction pressure welding, resistance welding, and brazing, a bonded portion is heated. Accordingly, a strength of a material forming the shank portion may vary due to a thermal effect, and cemented carbide may be oxidized. That is, an annealing effect may occur due to an increase in temperature of the bonded portion, and thus the strength of the shank portion may decrease and an oxide film may be generated on a surface of cemented carbide.
- When a material forming the shank portion is martensitic stainless steel or carbon steel that may expect hardening from a heat treatment, the strength can be improved by performing heat treatment again after the bonding. However, martensitic stainless steel or carbon steel has problems that the generation of rust cannot be excluded and a fracture is likely to be generated when hardness is excessively increased by heat treatment.
- In particular, from the viewpoint of preventing the generation of rust, it is preferable that austenitic stainless steel be used as a material of the shank portion. However, this material may not have an improved strength from heat treatment. Thus, the strength is improved by extending a structure to a fiber shape by a cold drawing process. However, when a structure extended in a fiber shape changes to a granular structure, the strength may be degraded.
- An object of the invention is to provide a medical cutting tool in which rust is not be generated, a fracture is hardly generated, and a high strength is stably exhibited.
- A medical cutting tool according to the invention to resolve the above problems is a medical cutting tool formed by brazing a working portion formed of cemented carbide or ceramic to a leading end of a shank portion formed by a round austenitic stainless steel bar, wherein the shank portion includes a shank, a neck formed to be continuous to the shank, and a joint which is formed to be continuous to neck and brazes the working portion formed of cemented carbide or ceramic, and at least a portion of stainless steel in the joint and near the joint of the neck includes a structure of a fiber shape.
- In the medical cutting tool described above, it is preferable that a structure of the stainless steel in the joint at a side of the working portion be a granular structure.
- In the medical cutting tool according to the invention, the shank portion is formed of austenitic stainless steel, and includes the shank, the neck, and the joint, and at least a portion of stainless steel in the joint and near the joint of the neck has a structure of a fiber shape. Thus, it is possible to sufficiently resist bending or warping acting when the working portion presses and cuts a hard layer.
- In addition, since the structure at the side of the working portion of stainless steel in the joint is a granular structure, the joint at the side of the working portion is in an annealing state, and thus flexibility can be exhibited and a fracture can be difficult to be generated.
-
FIG. 1 is a diagram illustrating a configuration of a cutting tool. -
FIG. 2 is an enlarged view illustrating a state in which a material of a working portion is brazed to a brazing surface of a shank portion. -
FIG. 3 is a diagram illustrating a configuration in which gas is sprayed to a brazing region and near the brazing region to perform cooling. -
FIG. 4 is a diagram illustrating a process order when the cutting tool is manufactured. -
FIG. 5 is a diagram illustrating a measurement position of hardness in a neck of the cutting tool. -
FIG. 6 is a diagram illustrating a structure of the brazing region of the cutting tool. -
-
- A Cutting tool
- 1 Shank portion
- 1 a Shank
- 1 b Neck
- 1 c Joint
- 1 d Brazing surface
- 2 Working portion
- 2 a Cutting blade
- 2 b Brazing surface
- 3 Brazing portion
- 5 a Apex
- 5 b Sloped surface
- 6 Solder
- 7 Material
- 8 Intermediate material
- 11 Chuck
- 12 Axis line
- 13 Holding member
- 13 a Holding hole
- 14 Heating member
- 15 Nozzle
- Hereinafter, a medical cutting tool (hereinafter, referred to as a “cutting tool”) of the invention will be described. The cutting tool of the invention is fixed to a chuck of a handpiece gripped and operated by a hand of a doctor to be rotated, so that a working portion presses a surface layer of a tooth or a surface of a bone including an alveolar bone to cut the surface layer or the surface.
- In particular, a favorable cutting performance is ensured by forming the working portion using cemented carbide or ceramic (hereinafter, represented by and referred to as “cemented carbide”), and at least a portion of stainless steel in a joint and near the joint of a neck forming a shank portion which is constructed by a round austenitic stainless steel bar (hereinafter, simply referred to as “stainless steel”) is formed in a structure of a fiber shape, thereby exhibiting high durability.
- In addition, in the cutting tool of the invention, a structure on a side of the working portion of a joint forming the shank portion is formed in a granular structure, thereby causing a side of the brazing portion in the joint to exhibit flexibility so that a fracture is hardly generated.
- In the cutting tool according to the invention, the shank portion is formed using a round stainless steel bar. The shank portion includes a shank, a neck formed to be continuous to the shank, and a joint formed to be continuous to the neck. In the shank portion, at a stage of an intermediate component preceding brazing of a material of cemented carbide forming the working portion, the shank and the neck are provided in the substantially same shape and size as those of a desired cutting tool, and the joint is provided in a size corresponding to a size of a material to be brazed. The shank portion is extremely thin, where the shank which is the thickest portion is about 1.6 mm and the thinnest portion in the neck is about 0.4 mm.
- The neck forming the shank portion has a function of smoothly connecting from the thickness of the shank to the thickness of the working portion (thickness of the joint). In a general cutting tool, the thickness of the shank is greater than the thickness of the working portion, and thus the neck is formed in a tapered shape where a diameter decreases from the shank to the joint.
- Since a great stress acts on the neck while a desired treatment is performed, a high strength is needed to be exhibited. The strength in the neck can be identified by conducting a test such as a tensile test and a flexural test. However, the inventor verifies a relation among the Vickers hardness, the strength needed for the cutting tool, and the extension of a fiber of a structure entailed by a cold drawing process as a result of various experiments conducted in a developmental process of the cutting tool over the years.
- That is, after the cold drawing process, it is verified that both a granular structure and a fiber shaped structure are included when the Vickers hardness of stainless steel is around 200, and a structure is extended in a fiber shape when the Vickers hardness is greater than or equal to 250. In addition, it is verified that it is possible to sufficiently resist bending and a warping that act on the neck when the Vickers hardness of stainless steel in the neck is greater than or equal to 350 and the working portion presses and cuts a tooth. However, it is verified that the Vickers hardness has an upper limit which is about 650 at the maximum, and in particular, it is preferable that the Vickers hardness is in the range of 350 or more and 600 or less because there occurs a problem that a fracture is easily generated when the hardness is excessively high.
- Accordingly, stainless steel forming the shank portion needs to be able to have the Vickers hardness in the neck in the range of 350 or more and 650 or less. For this reason, the cold drawing process is performed in advance on the stainless steel forming the shank portion, and a structure is extended in a fiber shape. In this way, by extending the structure in a fiber shape, it is possible to form at least a portion of stainless steel in the joint and near the joint of the neck in a structure of a fiber shape.
- Further, the surface of the stainless steel, in which a structure is extended in a fiber shape by performing the cold drawing process, needs to have a sufficiently great value than the Vickers hardness of 350. When the surface of austenitic stainless steel has such hardness, it is possible to provide the Vickers hardness of the neck of 350 or more and the fiber shaped structure by cutting a portion corresponding to the neck in forming the shank portion.
- Tungsten carbide (WC) or titanium carbide used as a cutting tool in machine processing may be employed as cemented carbide forming the working portion, and carbide ceramics represented by cermet may be employed as ceramic. The cemented carbide is brazed to the joint formed at a leading end of the shank portion in a state of a material. Thereafter, in a state in which the shank is gripped, machine processing is performed to have a size corresponding to a desired cutting tool, and machine processing of forming a spiral-shaped cutting blade is performed. Therefore, when a material of the working portion is brazed to the shank portion, the shank and the neck forming the shank portion substantially have a shape and a size corresponding to a desired cutting tool. However, a material of the joint and the working portion does not have a shape of the desired cutting tool, and has a large size.
- In the invention, a material of a solder used when the joint of the shank portion and a material of the working portion are brazed is not particularly limited. However, considering an influence of a brazing temperature with respect to the shank portion, a silver solder that melts at a relatively low temperature (for example, about 700° C.) is preferable. In addition, a property of the solder is not particularly limited, and any of a foil shape, a bar shape, and a paste shape may be used. However, a solder in a paste shape is preferable since a thickness of the joint of the shank portion or a material of the working portion is thin, and a void is small.
- When a material of the working portion is brazed to the joint of the shank portion, typically, cemented carbide which is the material of the working portion is heated in general. In this case, examples of a scheme of heating the material of the working portion formed of cemented carbide or ceramic include a heat scheme using a flame, a heat scheme of accommodating the material in a holding furnace, a heat scheme using an electromagnetic induction, and the like, and a scheme may be selected and employed from the schemes.
- In the invention, the material of the working portion is brazed to the joint forming the shank portion. Thus, due to heat given during the brazing, a temperature of the joint on the side of the working portion increases to an annealing temperature, and the temperature of the joint and the neck near the joint increases to an annealing temperature depending on a heating temperature and a heating time.
- Since the structure of stainless steel forming the shank portion is extended in a fiber shape, the joint on the side of the working portion is annealed so that the structure becomes a granular structure. When the structure of the joint on the side of the working portion is a granular structure, the granular structure portion exhibits flexibility so that a fracture is hardly generated.
- In particular, since the structure is stainless steel extended in a fiber shape, due to heat entailed by a brazing of cemented carbide which is a material of the working portion for the joint, both the joint and the neck are annealed, and thus a structure of a fiber shape may become a granular structure. Thus, it is preferable that a brazing region of stainless steel forming the shank portion and the neighborhood be forcibly cooled down.
- As described above, by forcibly cooling down the brazing region of stainless steel including the structure extended in a fiber shape while performing brazing, it is possible to prevent the temperature of the shank portion including the joint from excessively increasing. Accordingly, the structure of the fiber shape in the neck can be maintained, and the strength of the neck can be maintained.
- Next, an overall configuration of the cutting tool according to the embodiment will be described with reference to
FIG. 1 . - Referring to
FIG. 1 , a cutting tool A includes ashank portion 1 fixed to a chuck of a handpiece (not illustrated), and a workingportion 2 that cuts a surface layer of a tooth (not illustrated). Theshank portion 1 is made from stainless steel in which a structure is extended in a fiber shape, and the workingportion 2 is made from WC as a material. The cutting tool A is constructed when theshank portion 1 and the workingportion 2 are connected and integrated with each other through abrazing portion 3 using brazing. - The
shank portion 1 of the cutting tool A is fixed to the chuck of the handpiece (not illustrated), and rotates in this state. For this reason, ashank 1 a fixed to the chuck of the handpiece is formed on one side of theshank portion 1. Theshank 1 a has a constant thickness (a thickness of about 1.6 mm in the embodiment) corresponding to the size of the chuck regardless of the shape, the thickness, and the length of the workingportion 2. - A specification such as an external shape, a thickness, and a length of the working
portion 2 in the cutting tool A is set according to a therapeutic purpose of a portion or a degree to be cut. Thus, the cutting tool A illustrated inFIG. 1 is merely an example of the cutting tool A. For example, a shape of the workingportion 2 includes a round bar shape illustrated inFIG. 1 in which a leading end has a spherical shape and a thickness is uniform, a tapered shape in which a leading end has a spherical shape and a thickness becomes thinner toward the leading end, a sphere shape, and the like. A plurality of spiral-shapedcutting blades 2 a is formed on an outer circumference surface of the workingportion 2. - As described above, an external diameter of the working
portion 2 is set to various values corresponding to the purpose of the cutting tool A. Thus, as illustrated inFIGS. 2 and 4 , amaterial 7 of cemented carbide used to form the workingportion 2 corresponding to the cutting tool A (hereinafter, simply referred to as “material 7”) is brazed to the leading end of theshank portion 1 corresponding to the desired cutting tool A in advance, and then machine processing such as cutting and grinding is performed on the leading end portion of theshank portion 1 and thematerial 7, thereby providing a shape and a size corresponding to the desired workingportion 2. - Thus, in the
shank portion 1, aneck 1 b in a tapered shape is formed to be continuous to theshank 1 a having a constant thickness, and a joint 1 c having a diameter substantially equal to or slightly less than a thickness of thematerial 7 is formed at a leading end of theneck 1 b. A thickness of the joint 1 c is not particularly limited, and one third of a diameter of the joint 1 c or less is sufficient for the thickness. As illustrated inFIG. 2 , abrazing surface 1 d is formed on an edge face of the joint 1 c, and asloped surface 5 b having an apex 5 a is formed on thebrazing surface 1 d. - The
sloped surface 5 b having the apex 5 a formed on thebrazing surface 1 d of theshank portion 1 is formed as a sloped surface having a circular cone shape for an easiness of processing. By forming thesloped surface 5 b in a circular cone shape, thebrazing surface 1 d may be fabricated concurrently with a fabrication of another portion, for example, theneck 1 b and the joint 1 c when theshank portion 1 is rotated and cut from a stainless steel material having a round bar shape, which is advantageous. - As a result of various experiments conducted by the inventor, as one of conditions for being able to exhibit a practical bending strength by the
brazing portion 3, a relation between a height of the slopedsurface 5 b in thebrazing portion 3 and a thickness of thebrazing portion 3 is confirmed to be present. That is, referring to the relation, it is preferable that the height of the slopedsurface 5 b be set in the range of 0.5% to 8% of the diameter of the brazing surface. When the height is less than a value in the range, an amount of solder is small, and thus the sufficient joint strength is difficult to be obtained. In addition, when the height is greater than a value in the range, an amount of solder is large, and thus workability deteriorates, cost increases, and variation occurs in a joint strength. In particular, to obtain a uniform and sufficiently great joint strength, it is preferable that the height of the slopedsurface 5 b provided on thebrazing surface 1 d be set in the range of 1% to 5% of a diameter of thebrazing surface 1 d. - For this reason, in a case of the cutting tool A in which the thickness of the working
portion 2 is 1.2 mm, the height of the slopedsurface 5 b is 0.038 mm, and is set to be about 3.1% of the thickness of the workingportion 2. In addition, in a case of the cutting tool A in which the thickness of the workingportion 2 is 1.0 mm, the height is 0.031 mm, and is set to be about 3.1% of the thickness of the workingportion 2. Further, in a case of the cutting tool A in which the thickness of the workingportion 2 is 0.8 mm, the height is 0.022 mm, and is set to be about 2.8% of the thickness of the workingportion 2. - In addition, the
brazing surface 2 b is formed on an edge face at the side of theshank portion 1 of the working portion 2 (material 7). The shape of thebrazing surface 2 b is not particularly limited, and may be a flat surface or the same shape as that of thebrazing surface 1 d of theshank portion 1. In the embodiment, as illustrated inFIG. 2 , thebrazing surface 2 b of the workingportion 2 is formed as a flat surface. - The
shank portion 1 and thematerial 7 are disposed in which thebrazing surface 1 d formed at the joint 1 c of theshank portion 1 and thebrazing surface 2 b formed on an edge face of thematerial 7 face each other in thebrazing portion 3, and are bonded to each other by thesolder 6 supplied to a void formed between the brazing surfaces 1 d and 2 b and hardened. - In particular, by causing the apex 5 a of the sloped
surface 5 b formed on thebrazing surface 1 d of theshank portion 1 to come into contact with thebrazing surface 2 b of thematerial 7, the void between the brazing surfaces 1 d and 2 b is set to a size identical to the height of the slopedsurface 5 b. Accordingly, a volume of the void in thebrazing portion 3 is substantially constant, and a supplied amount of thesolder 6 may be stable. - When the
shank portion 1 and thematerial 7 are brazed and bonded to each other, thebrazing portion 3 is heated to a melting temperature of thesolder 6, and thesolder 6 is melted due to an increased temperature in thebrazing portion 3, so that the void formed between the brazing surfaces 1 d and 2 b is filled. Then, when heating of thebrazing portion 3 is suspended, thebrazing portion 3 is cooled down, and thesolder 6 is hardened, so that theshank portion 1 and thematerial 7 are bonded to each other. Thereafter, the cutting tool A is constructed by performing predetermined machine processing on thematerial 7. - In the cutting tool A constructed as described above, the
neck 1 b has the hardness greater than or equal to the Vickers hardness 350, and it is possible to exhibit the sufficient strength with respect to the bending stress and the torsional force acting when a desired cutting operation is performed by the workingportion 2. - For example, when the Vickers hardness of the
neck 1 b is less than or equal to 350, the neck portion is bent, and a stable cutting is difficult, which is not preferable. However, an unlimitedly high hardness of theneck 1 b is not preferable. For example, when the Vickers hardness exceeds 650, a fracture is easily generated, which is not preferable. - Next, a procedure of manufacturing the cutting tool A constructed as described above will be described. In the embodiment, while a brazing operation is performed, a neighborhood of the brazing region is forcibly cooled down, thereby preventing an annealing of the
neck 1 b in theshank portion 1 to maintain a structure extended in a fiber shape, and maintaining the Vickers hardness greater than or equal to 350. - In the embodiment, the joint 1 c and a joint part between the joint 1 c and the
neck 1 b are collectively referred to as a brazing region. In addition, a neighborhood of the joint 1 c in theneck 1 b includes the joint part between the joint 1 c and theneck 1 b, is a portion included in a neighborhood of the brazing region, and is a portion about twice a thickness of the joint 1 c. - When the
material 7 of the workingportion 2 is brazed to theshank portion 1 formed from stainless steel, a scheme of cooling down the brazing region and the neighborhood of the brazing region are not particularly limited. A cooling scheme that may maintain the brazing region and the neighborhood of the brazing region at a temperature less than or equal to a transformation temperature of a structure may be used. That is, a transformation of austenitic stainless steel may occur from about 500° C., and thus a cooling scheme that may maintain the temperature or less by forcibly cooling down the brazing region and the neighborhood of the brazing region in theshank portion 1 may be employed. - Examples of the cooling scheme include a cooling scheme that sprays gas having a pressure, a cooling scheme that sprays liquid as a mist, a cooling scheme that directly sprays liquid, a cooling scheme that sprays a dry ice chip or an ice chip, and a cooling scheme that disposes a cooling medium at the brazing region and the neighborhood of the brazing region, and sprays wind through the cooling medium. A cooling scheme may be selected and employed from the cooling schemes.
- In addition, when the
shank portion 1 is formed using stainless steel, and the workingportion 2 is formed using cemented carbide which is formed from WC, it is preferable that an oxidization of a surface of the stainless steel and a surface of the cemented carbide occurring during a brazing operation be reduced as possible. For this reason, it is preferable that an inert gas be sprayed when forcibly cooling down the brazing region or the neighborhood of the brazing region in stainless steel. - In this case, it is preferable that gas generally used as an inert gas such as nitrogen gas and argon gas be used as the inert gas. However, an object of spraying an inert gas is to prevent an oxidization of a surface of stainless steel and a surface of cemented carbide, and thus gas which is inert at a degree capable of achieving the object may be used. That is, 100% nitrogen gas or argon gas may not be used as an inert gas, and gas in which nitrogen gas or argon gas and air are mixed may be used.
- In addition, when the
shank portion 1 and thematerial 7 of the workingportion 2 are brazed, gas is generated due to an increased temperature of a solder. Thus, as an example of the embodiment, by forming thesloped surface 5 b including the apex 5 a on thebrazing surface 1 d formed on the edge face of the joint 1 c of theshank portion 1, the generated gas may be smoothly removed from a brazing part. In particular, when a brazing operation is performed, by causing the apex 5 a to come into contact with the edge face of thematerial 7, a gap therebetween may be maintained. - Further, when the
shank portion 1 and thematerial 7 of the workingportion 2 are brazed, it is preferable that cemented carbide forming thematerial 7 be disposed in the bottom for supporting, and theshank portion 1 be substantially perpendicularly disposed to cause the apex 5 a to come into contact with the edge face of thematerial 7. When disposed in this position, gas generated during a brazing rises along the slopedsurface 5 b and is vented to atmosphere from an outer circumference of the joint 1 c. In addition, a melted solder penetrates into a small part by capillary phenomenon acting on a minute void formed from a slope of the protrusion portion and the edge face of the working portion, and an excellent brazing may be realized. - By providing the
sloped surface 5 b including the apex 5 a on thebrazing surface 1 d of theshank portion 1, a gap between thebrazing surface 1 d and the edge face of the material 7 (brazing surface) may be set during a brazing operation, and the gap may be maintained through the brazing operation. Thus, the brazing operation may be performed while the gap between thebrazing surface 1 d and the edge face of thematerial 7 is stably maintained, and a variation in strength resulting from the brazing operation may be excluded. - A shape of the sloped
surface 5 b including the apex 5 a provided on thebrazing surface 1 d is not particularly limited. Examples of the shape include a curved surface shape, a circular cone shape, a pyramid shape, and the like, and a shape including the shapes may be used. However, considering at least a condition of easiness and the like of processing when theshank portion 1 is formed, it is preferable to be formed as a circular cone shape. - The
sloped surface 5 b including the apex 5 a provided on thebrazing surface 1 d of theshank portion 1 is brazed in a state of coming into contact with an opposing brazing surface (the edge face of the material 7). Thus, a height of the slopedsurface 5 b defines a gap between two opposing brazing surfaces, and sets a volume of a solder in the brazing portion. For this reason, it is preferable that the height of the slopedsurface 5 b be changed in response to the thickness in the joint portion between theshank portion 1 and the workingportion 2. - A configuration of a brazing device suitably used when the
shank portion 1 and thematerial 7 forming the workingportion 2 are brazed as described above, and a procedure of a brazing using the brazing device will be described with reference toFIG. 3 . The brazing device illustrated inFIG. 3 is configured so as to be able to forcibly cool down a brazing region of theshank portion 1 and thematerial 7, and a neighborhood of the brazing region by spraying an inert gas. - Referring to
FIG. 3 , achuck 11 is configured to be able to reciprocate along anaxis line 12 by gripping theshank 1 a of theshank portion 1. A holdingmember 13 is configured to be able to put and hold thematerial 7 of the workingportion 2 in a holdinghole 13 a formed on theaxis line 12. Aheating member 14 is configured to be able to heat thematerial 7 held in the holdinghole 13 a of the holdingmember 13 by a coil in a ring shape. - A
nozzle 15 is configured to spray an inert gas to forcibly cool down a brazing region of thebrazing surface 1 d formed at the joint 1 c of theshank portion 1 and thematerial 7 of the working portion, and a neighborhood of the brazing region. As the inert gas sprayed from thenozzle 15, nitrogen gas, argon gas, and the like may be selectively used. For this reason, a source of supply of an inert gas (not illustrated) is connected to thenozzle 15. - The number of
nozzles 15 is not limited, and may be one, or two or more. Thenozzle 15 is needed to be disposed to be able to evenly cool down a brazing region in theshank portion 1 and theneck 1 b which is a neighborhood of the brazing region. In addition, a temperature of an inert gas sprayed from thenozzle 15 is not limited, and a sufficient cooling effect may be exhibited even when an inert gas in a normal temperature state is sprayed. - An amount of inert gas sprayed from the
nozzle 15 is preferably large. However, it is preferable to be appropriately set from a relation with a scheme of heating thebrazing portion 3. For example, in a case of a heating scheme using a combustion flame of gas, a stable combustion flame may be difficult to be formed when a flow rate of an inert gas increases, and a current speed increases. However, in a case of a scheme using an induction heating as an example of the embodiment, a high cooling effect may be exhibited by spraying an inert gas of a sufficiently large flow rate. - As illustrated in
FIGS. 2 and 3 , first, thematerial 7 is put into the holdinghole 13 a of the holdingmember 13, and theshank 1 a of theshank portion 1 is gripped by thechuck 11. Thesolder 6 is supplied to thebrazing surface 2 b which is the edge face of thematerial 7, thechuck 11 is caused to descend along theaxis line 12, and the apex 5 a of the slopedsurface 5 b formed on thebrazing surface 1 d of theshank portion 1 is caused to come into contact with thebrazing surface 2 b. - When an inert gas is sprayed from the
nozzle 15 by maintaining the state, the brazing region in theshank portion 1 and theneck 1 b which is a neighborhood of the brazing region are cooled down. - Further, the
material 7 of the workingportion 2 is heated for a short period of time by operating theheating member 14, and thesolder 6 is melted due to the heating to flow to and fill the void formed by the slopedsurface 5 b provided on thebrazing surface 1 d of theshank portion 1, and the edge face of thematerial 7. In addition, gas generated due to the melting of thesolder 6 moves upward along the slopedsurface 5 b, arrives at the circumference surface of the joint 1 c, and then is vented to atmosphere. - The
heating member 14 is operated for a predetermined time (for example, about greater than or equal to 1 second and less than or equal to 5 seconds), and the operation of theheating member 14 is suspended after the meltedsolder 6 sufficiently flows to fill the void formed by the slopedsurface 5 b and the edge face of thematerial 7. Thesolder 6 is hardened due to the suspension of the operation of theheating member 14, and a brazing operation is ended. - As described in the foregoing, while the
heating member 14 is operated, and the brazing operation is performed, an inert gas is sprayed to the brazing region in theshank portion 1 and theneck 1 b which is a neighborhood of the brazing region to forcibly cool down the brazing region and theneck 1 b. For this reason, even though heat entailed by the brazing is transferred to theneck 1 b, an increase in temperature may be inhibited, and recrystallization of a structure extended in a fiber shape may be prevented. Since a structure of theneck 1 b maintains a state of being extended in a fiber shape, the Vickers hardness of 350 or more is maintained, and a strength as the cutting tool A may be maintained. - As describe above, the
material 7 of the workingportion 2 brazed to theshank portion 1 may not have a shaft center accurately matching a shaft center of theshank portion 1. For this reason, as illustrated inFIG. 4 , the desired cutting tool A is manufactured by performing machine processing including a cutting or a grinding on thematerial 7. - That is, as illustrated in
FIG. 4( a), thematerial 7 of cemented carbide sufficiently greater than a thickness and a length of the desired workingportion 2 is brazed to thebrazing surface 1 d formed at the joint 1 c of theshank portion 1, and then anintermediate material 8 is constructed by processing thematerial 7 as illustrated inFIG. 4( b). This operation is fixing theshank 1 a of theshank portion 1 to a processing equipment (not illustrated), and grinding thematerial 7 so that the workingportion 2 has a desired thickness while causing a rotation in this state. As described above, since a center of rotation of theshank 1 a of theshank portion 1 is a center of rotation of the cutting tool A, a center of rotation of theintermediate material 8 accurately matches the center of rotation of theshank portion 1 even when a center of rotation of thematerial 7 does not match the center of rotation of theshank portion 1. - Next, as illustrated in
FIG. 4( c), theintermediate material 8 is processes to form a hemispherical edge, and the spiral-shapedcutting blades 2 a are formed on a circumference surface. Through the processing, the workingportion 2 is formed of thematerial 7 through theintermediate material 8, thereby manufacturing the desired cutting tool A. - The inventors measured the Vickers hardness of the
neck 1 b in the cutting tool A formed by forcibly cooling down the brazing region in theshank portion 1 and theneck 1 b which is a neighborhood of the brazing region, and the Vickers hardness of theneck 1 b in a cutting tool formed without forcibly cooling down theneck 1 b, and compared the Vickers hardness. The result will be described. - Ten cutting tools of a specification illustrated in
FIG. 5 are fabricated as test pieces. A minimum size of theneck 1 b inFIG. 5 is 1.02 mm. Five test pieces among the ten test pieces are fabricated by spraying nitrogen gas of 5 normal liters per minute to the brazing region in theshank portion 1 and a neighborhood of the brazing region, and forcibly cooling down the brazing region and the neighborhood. The remaining five pieces are fabricated without being cooled down. - As a brazing region in each test piece, an intersection part of the
neck 1 b and the joint 1 c of theshank portion 1 is set, and the hardness is measured for four points (0, 0.7, 1.4, and 2.1) from this part for each 0.7 mm. A measurement scheme of hardness is based on JIS Z2244 (2003). The Vickers hardness is HV0.3, a test pressure is 2.942 N, and a holding time of the test pressure is 15 seconds. - As a result of the test, the Vickers hardness of the five cooled pieces is in a range of 367 to 412 at the point 0, in a range of 475 to 503 at the point 0.7, in a range of 504 to 533 at the point 1.4, and in a range of 516 to 550 at the point 2.1. In addition, the Vickers hardness of the five pieces that are not cooled is in a range of 285 to 299 at the point 0, in a range of 334 to 343 at the point 0.7, in a range of 439 to 453 at the point 1.4, and in a range of 484 to 508 at the point 2.1.
- From a result of the test, it is clarified that the Vickers hardness of 350 or more of the
neck 1 b may be realized by forcibly cooling down the brazing region and a neighborhood of the brazing region. In theneck 1 b having the Vickers hardness of 350 or more, it can be presumed that a structure maintains a state of being extended in a fiber shape. - In addition, ten cutting tools in which a length of the
neck 1 b ofFIG. 5 is 6.3 mm, and a minimum size of theneck 1 b is 0.62 mm are fabricated as test pieces. Similarly to the above test, five test pieces among the ten test pieces are fabricated by spraying nitrogen gas of 5 normal liters per minute to the brazing region in theshank portion 1 and a neighborhood of the brazing region, and forcibly cooling down the brazing region and the neighborhood. The remaining five pieces are fabricated without being cooled down. Then, the hardness for four points are measured under the same condition as described above. - As a result of the test, the Vickers hardness of the five cooled pieces is in a range of 357 to 376 at the point 0, in a range of 460 to 478 at the point 0.7, in a range of 533 to 544 at the point 1.4, and in a range of 550 to 558 at the point 2.1. In addition, the Vickers hardness of the five pieces that are not cooled is in a range of 260 to 283 at the point 0, in a range of 318 to 342 at the point 0.7, in a range of 404 to 430 at the point 1.4, and in a range of 502 to 532 at the point 2.1.
- From the result of the test, it is clarified that the Vickers hardness of 350 or more of the
neck 1 b may be realized by forcibly cooling down the brazing region and a neighborhood of the brazing region even for the cutting tool in which a length of theneck 1 b is 6.3 mm, and a minimum size of theneck 1 b is 0.62 mm. In theneck 1 b having the Vickers hardness of 350 or more, it may be presumed that a structure maintains a state of being extended in a fiber shape. - In the cutting tool A formed as described above, the joint 1 c forming the
shank portion 1 at the side of the working portion is in a granular structure.FIG. 6 is an enlarged view of the structure of thebrazing portion 3 in a longitudinal direction (a direction that cuts theshank portion 1, thesolder 6, and the workingportion 2 longitudinally) of the cutting tool A. The joint 1 c at the side of the workingportion 2 is in a granular structure at a range of a depth of several μm, and another portion maintains a structure of a fiber shape. - A cutting tool of the invention is formed by brazing and bonding a working portion formed of cemented carbide or ceramics to a leading end of a shank portion formed by a round austenitic stainless steel bar, and at least a portion of stainless steel in a joint and near the joint of the neck includes a structure of a fiber shape, and thus the neck has a sufficient strength for a bending and a warping. For this reason, it is advantageous to be used when cutting a hard layer such as a tooth.
Claims (2)
1. A medical cutting tool formed by brazing a working portion formed of cemented carbide or ceramics to a leading end of a shank portion formed by a round austenitic stainless steel bar,
wherein the shank portion includes a shank, a neck formed to be continuous to the shank, and a joint which is formed to be continuous to the neck and which brazes the working portion formed of cemented carbide or ceramics, and
at least a portion of stainless steel in the joint and near the joint of the neck includes a structure of a fiber shape.
2. The medical cutting tool according to claim 1 , wherein a structure of the stainless steel in the joint at a side of the working portion is a granular structure.